Herein, epitaxially regrown n+ (In)GaN source/drain layers for radio frequency high electron mobility transistors, addressing material and electrical characterization, are reported. A range of n+ GaN and n+ InGaN layers with indium 4–12 at\% and silicon 0–5.1 × 1020 cm−3 are evaluated. The active carrier concentration in n+ InGaN exceeds 2 × 1020 cm−3. The layers exhibit so-called V-defects, observed by atomic force microscope and transmission electron microscope (TEM), which are associated with local composition changes. In addition to the high Si doping levels, nitrogen vacancies are also considered to contribute toward their net carrier concentration. Due to its relevance for device processing, selectivity analysis is performed, and the optimal process conditions for selective regrowth are identified. Regrowth under high temperature (800 °C) is found to be conducive to improved selectivity. However, a high thermal budget negatively impacts the overall regrowth process, as reported here for In0.17Al0.83N and Al0.26Ga0.74N barriers: whereas the InAlN barrier suffers from intermixing, the AlGaN barrier demonstrates high-temperature stability. The impact of intermixing is studied from complementary TEM and DC electrical measurements. A low overall contact resistance of 75 Ω μm is obtained with the regrown n+ InGaN layers.
Banerjee, S, Peralagu, U, Alian, A, Zhao, M, Hahn, H, Minj, A, Vanhove, B, Vohra, A, Parvais, B, Langer, R & Collaert, N 2024, 'Metal-Organic Chemical Vapor Deposition Regrowth of Highly Doped n+ (In)GaN Source/Drain Layers for Radio Frequency Transistors', Physica Status Solidi (A) Applications and Materials Science, vol. 221, no. 21, 2400069. https://doi.org/10.1002/pssa.202400069
Banerjee, S., Peralagu, U., Alian, A., Zhao, M., Hahn, H., Minj, A., Vanhove, B., Vohra, A., Parvais, B., Langer, R., & Collaert, N. (2024). Metal-Organic Chemical Vapor Deposition Regrowth of Highly Doped n+ (In)GaN Source/Drain Layers for Radio Frequency Transistors. Physica Status Solidi (A) Applications and Materials Science, 221(21), Article 2400069. https://doi.org/10.1002/pssa.202400069
@article{8271c8b2b7b94d0f8389e5a42833fcb2,
title = "Metal-Organic Chemical Vapor Deposition Regrowth of Highly Doped n+ (In)GaN Source/Drain Layers for Radio Frequency Transistors",
abstract = "Herein, epitaxially regrown n+ (In)GaN source/drain layers for radio frequency high electron mobility transistors, addressing material and electrical characterization, are reported. A range of n+ GaN and n+ InGaN layers with indium 4–12 at\% and silicon 0–5.1 × 1020 cm−3 are evaluated. The active carrier concentration in n+ InGaN exceeds 2 × 1020 cm−3. The layers exhibit so-called V-defects, observed by atomic force microscope and transmission electron microscope (TEM), which are associated with local composition changes. In addition to the high Si doping levels, nitrogen vacancies are also considered to contribute toward their net carrier concentration. Due to its relevance for device processing, selectivity analysis is performed, and the optimal process conditions for selective regrowth are identified. Regrowth under high temperature (800 °C) is found to be conducive to improved selectivity. However, a high thermal budget negatively impacts the overall regrowth process, as reported here for In0.17Al0.83N and Al0.26Ga0.74N barriers: whereas the InAlN barrier suffers from intermixing, the AlGaN barrier demonstrates high-temperature stability. The impact of intermixing is studied from complementary TEM and DC electrical measurements. A low overall contact resistance of 75 Ω μm is obtained with the regrown n+ InGaN layers.",
keywords = "drain, GaN, InGaN, metal-organic chemical vapor deposition, n contact, regrowth, source",
author = "Sourish Banerjee and Uthayasankaran Peralagu and Alireza Alian and Ming Zhao and Herwig Hahn and Albert Minj and Benjamin Vanhove and Anurag Vohra and Bertrand Parvais and Robert Langer and Nadine Collaert",
note = "Publisher Copyright: {\textcopyright} 2024 Wiley-VCH GmbH.",
year = "2024",
month = nov,
doi = "10.1002/pssa.202400069",
language = "English",
volume = "221",
journal = "Physica Status Solidi (A) Applications and Materials Science",
issn = "1862-6300",
publisher = "Wiley-VCH Verlag",
number = "21",
}